STORAGE AND HANDLING

Rolls should be stored In their original wrapping on pallets in dry closed sun protected place minimum 1 meter from heating units.

Storage conditions should eliminate any risk of wrapping deterioration. If stored in unheated area Biaxplen films should be placed at room temperature and humidity at least for 48 hours before converting.

It’ is recommended to corona pre treat fi lm before printing Guaranteed storage life is 6 months from the date of production.

SURFACE TREATMENT

Metallized film surface energy Is affected by temperature and storage life. Biaxplen guarantees surface treatment level of metallized films higher than 36 dynes within 15 days after metallization. In order to minimize the deterioration of surface energy it is recommended to store film below 30°C and to convert it asap. Should film be used for specific application, it is advisable to measure surface energy in order to prove if it suits. Standard roll- outside corona treated web. Metallized film is advised to be primer covered before printing. Metallized film can be laminated with a number of materials.

It’s highly recommended that the film should be used according to the application recommended by the Producer.

Information given in Techical data sheets is based on typical values checked in standard production. Techical data sheet has not to be considered a product specification.

DIMENSIONS

Application Max outer diameter, mm Core diameter, mmTolerance
Width, mm Order weight
For tobacco films 500 76
120
152
± 0,5 ± 10%*
450
400
300< 2000 kg ± 20%
For all packaging films 980 76
52
± 3 mm > 2000 kg ± 10%
780 > 5000 kg ± 5%
580± 2 m >10000 kg ± 2%
Biaхplen LGBA

DESCRIPTION:

Transparent BOPP film for labels and for general applications for bonding by cold and hot melt adhesives when labelling with improved ink adhesion for printing.

pgr.JPG

1. Treated side of modified copolymer skin layer.

2. Transparent biaxially oriented polypropylene.

3. Glossy, none treated, none heat sealable polypropylene skin layer with standard coefficient of friction.



MAIN PROPERTIES:

  • Improved ink adhesion;
  • Contains antistatic and slip- antiblocking agents;
  • excellent optical properties: transparency and gloss;
  • good mechanical properties;
  • permanent coefficient of friction;
  • without coating or primer.

APPLICATION:

  • High quality solvent based rotogravure and flexographic printing;
  • for production of fully wrapped labels for bottles;
  • for labeling with cold and hot melt glue;
  • solvent based and solvent free lamination with polyurethane adhesives (if necessary).
Documentation
Biaхplen LOBA

DESCRIPTION:

White Pearlised microporous BOPP film for fully wrapped labeling of bottles for cold and hot melt glue application while labeling with good gloss and ink adhesion.

hasl.JPG

1. Modified copolymer corona treated skin layer.

2. White opaque oriented polypropylene tie layer.

3. White Pearl cavitated core layer of oriented polypropylene.

4. Oriented polypropylene tie layer.

5. Glossy non heat sealable, non treated skin layer with standard coefficient of friction.

MAIN PROPERTIES:

  • High adhesion of solvent based inks: flexo and rotogravure for direct printing;
  • both side glossy film;
  • good opacity and whiteness;
  • contains slip, antistatic and antiblock additives;
  • contains mineral fillers such as calcium carbonate and titanium dioxide;
  • low coefficient of friction, stable in time;
  • without coating or primer.

APPLICATION:

  • High quality solvent rotogravure and flexographic direct printing;
  • for production of fully wrapped labels for bottles;
  • for labeling with cold and hot melt glue.
Documentation
Biaхplen LOBB

DESCRIPTION:

White Pearlised microporous glossy BOPP film for fully wrapped labeling of bottles for cold and hot melt glue application while labeling with excellent gloss and high ink adhesion.

hasl.JPG

1. Modified copolymer corona treated glossy skin layer.

2. Oriented polypropylene tie layer.

3. White Pearl cavitated core layer of oriented polypropylene.

4. Oriented polypropylene tie layer.

5. Glossy non heat sealable, non corona treated skin layer with standard coefficient of friction.

MAIN PROPERTIES:

  • Both side excellent gloss;
  • high adhesion of solvent based inks: flexo and rotogravure for direct printing;
  • excellent opacity and whiteness;
  • with increased yield;
  • contains slip, antistatic and antiblock additives;
  • contains mineral fillers such as calcium carbonate and titanium dioxide;
  • low coefficient of friction, stable in time;
  • without coating or primer.

APPLICATION:

  • High quality solvent rotogravure and flexographic printing;
  • for production of fully wrapped labels for bottles;
  • for labeling with cold and hot melt glue.
Documentation
Biaхplen LOBC

DESCRIPTION:

White Pearlised microporous BOPP film for fully wrapped labeling of bottles for cold and hot melt glue application while labeling with very high yield good gloss and good ink adhesion.

hasl.JPG

1. Modified copolymer corona treated skin layer.

2. White opaque oriented polypropylene tie layer.

3. White Pearl cavitated core layer of oriented polypropylene.

4. Oriented polypropylene tie layer.

5. Glossy non heat sealable, non corona treated skin layer with standard coefficient of friction.

MAIN PROPERTIES:

  • Very low density and very high yield;
  • high adhesion of solvent based inks: flexo and rotogravure for printing;
  • both side glossy film;
  • good opacity and whiteness;
  • contains mineral fillers such as calcium carbonate and titanium dioxide;
  • contains slip, antistatic and antiblock additives;
  • low coefficient of friction, stable in time;
  • without coating or primer.

APPLICATION:

  • High quality solvent based rotogravure and flexographic printing;
  • for production of fully wrapped labels for bottles;
  • for labeling with cold and hot melt glue.
Documentation
Biaхplen LOHM.M

DESCRIPTION:

White Pearlised metallized microporous BOPP film for labeling of bottles, for cold and hot melt glue application while labeling.

hohmlb.m.JPG

1. High glossy aluminum layer.

2. Modified layer for aluminum adhesion.

3. Oriented polypropylene tie layer.

4. White Pearl cavitated core layer of orinted polypropylene.

5. Oriented polypropylene tie layer.

6. Glossy non heat sealable, non treated skin layer with standard coefficient of friction.

MAIN PROPERTIES:

  • Very smoth surface and high gloss metallized side;
  • excellent adhesion of the aluminum layer;
  • lower density, high opacity and good whiteness;
  • permanent coefficient of friction and good mechanical properties;
  • contains an organic dye pearl and non-migratory slip additives;
  • intended for contact with food;
  • without coating or primer.

APPLICATION:

  • High quality solvent based rotogravure and flexographic direct printing;
  • for production of fully wrapped labels for bottles;
  • for labeling with cold and hot melt glue.
Documentation
Biaхplen LOMB

DESCRIPTION:

Matt White Pearlised microporous BOPP film for fully wrapped labeling of bottles.

hasl.JPG

1. Matt white corona treated skin layer.

2. White opaque oriented polypropylene tie layer.

3. White Pearl cavitated core layer of oriented polypropylene.

4. Oriented polypropylene tie layer.

5. Glossy non heat sealable, non treated skin layer with standard coefficient of friction.

MAIN PROPERTIES:

  • Matt white, paper appearance;
  • high adhesion printing;
  • good opacity and whiteness;
  • contains slip, antistatic and antiblock additives;
  • contains mineral fillers such as calcium carbonate and titanium dioxide;
  • low coefficient of friction, stable in time;
  • without coating or primer.

APPLICATION:

  • High quality solvent based printing;
  • for production of fully wrapped labels of bottles;
  • for labeling with cold and hot melt glue.
Documentation